Product Description
Carbon Nanotube Masterbatches CNT-ABS-10
Our carbon nanotube masterbatches CNT-ABS-10 usees our industrial grade multi walled carbon nanotubes. This product has a 15% CNTs loading ratio.
The CNT-ABS-10 material can be used with 3D printers, injection molders, & extruders. Once received, you simply let it down and run it in your equipment. Sold by the kilogram
|
Product Code |
Matrix Resin |
Matrix Resin Loading |
CNTs Code |
CNTs Loading |
Resistivity (four probe method) |
|
CNT/ABS |
ABS 757 |
90wt% |
IGMWNTS |
10wt% |
8 ohm.cm |
CNTs were dispersed in ABS using twin-screw extruder, then the specimens were made by compression molding. Volume and surface resistivity were measured by high insulation resistance instrument ZC-90D（IEC 60093-1980, the test voltage is 100V).
-
CNTs Loading（wt%）
2.5
Volume Resistivity (ohm.cm)
1.1×109
Surface Resistivity (ohm)
3.2×107
CNTs were dispersed in ABS using twin-screw extruder, then the specimens were made by injection molding. The standard of mechanical property of specimens was ISO 527, ISO 180 and ISO 178.
|
CNTs Loading（wt%） |
0（Neat ABS） |
2.5 |
|
Tensile Strength（MPa） |
49.9 |
49.7 |
|
Stain at break（%） |
11 |
6 |
|
Izod Notched Impact Strength（KJ/m2） |
15.4 |
7.1 |
|
Flexural Strength（MPa） |
78 |
81 |
|
Flexural Modulus（MPa） |
2689 |
2888 |
|
Melt Index （g/10min，5Kg/220℃） |
19 |
12.8 |